TECAFIL PA6 GF30TECAFIL PA6 GF30

TECAFIL PA6 GF30

111,60 

To enable printing of engineering plastics on all types of printers, we have developed and qualified our TECAFIL PA6 GF30 black, a nylon filament reinforced with 30 % glass fibers.

Available on backorder

SKU: GETENSINGERPA6GF30 Categories: ,

TECAFIL PA6 GF30

To enable printing of engineering plastics on all types of printers, we have developed and qualified our TECAFIL PA6 GF30 black, a nylon filament reinforced with 30 % glass fibers.

To bridge the gap between standard and high temperature plastic filaments, Ensinger manufactures a modified PA6 filament, which is categorized as an engineering thermoplastic filament.
Our nylon 6 filament is available in 1,75 mm and 2,85 mm and is well suited for all industrial or desktop printers. Therefore, this filament is also qualified for Ultimaker printers like the S5 and S3. The recommended print temperature of 270 °C and a print bed temperature of 75 °C make it very easy to print end applications or prototypes in perfect quality. With its 30 % glass fiber volume, this material can be considered one of the strongest nylon filaments on the market in terms of mechanical strength.
Thanks to its good tensile strength, high stiffness, compressive strength and impact resistance, our glass-filled nylon filament enables a wide range of applications, such as structural parts or applications with high static loads and high temperature conditions over long periods of time. Especially where high stiffness and strength is a key requirement, such as in the automotive or electronics industry as well as in mechanical engineering, our PA6 GF30 filament is a perfect fit for your application.
Due to its high fiber volume, our PA filament can reduce the warpage of your printed application compared to conventional polyamide filaments.

FACTS

 

MAIN FEATURES

 

TARGET INDUSTRIES

 

Chemical designation
PA 6 (Polyamide 6)Colour
black

Density
1.36 g/cm3 (*2)

 

  • high strength
  • high dimensional stability
  • good weldable and bondable
  • good heat deflection temperature
  • resistant to many oils, greases and fuels

 

electronics

automotive industry

mechanical engineering

 

DOWNLOADS

DATASHEET (PDF)

PRODUCT HANDLING (PDF)

 

Weight 1 kg
Filament weight

Τεχνικά χαρακτηριστικά

GENERAL MATERIAL INFORMATION VALUE UNIT PARAMETER NORM
Diameter 2,85 +/- 0,05 mm
Spool measurements Ø 52 mm holder
Spool measurements 55 mm width
Spool measurements Ø 200 mm outer diameter
Spool Material Polycarbonate
Filament Load per Spool 750 g
MECHANICAL PROPERTIES VALUE UNIT PARAMETER NORM
Tensile strength 72 MPa 5mm/min, Orientation XY DIN EN ISO 527-2
Modulus of elasticity
(tensile test)
5200 MPa 5mm/min, Orientation XY DIN EN ISO 527-2
Elongation at break (tensile test) 5,0 % 5mm/min, Orientation XY DIN EN ISO 527-2
Flexural strength 115 MPa 2mm/min, Orientation XY DIN EN ISO 178
Modulus of elasticity
(flexural test)
4460 MPa 2mm/min, Orientation XY DIN EN ISO 178
THERMAL PROPERTIES VALUE UNIT PARAMETER NORM
Glass transition temperature 60 C ASTM D 3418
Melting temperature 220 C DIN EN ISO 11357
Deflection temperature C HDT-A ISO-R 75 Method A
Service temperature 180 C short term
Service temperature 100 C long term
Thermal expansion (CLTE) 6 10-5*1/K DIN EN ISO 11359-1;2
OTHER PROPERTIES VALUE UNIT PARAMETER NORM
Moisture absorption 0,3 % DIN EN ISO 62
Melt flow index (MFI) g/10 min DIN EN ISO 1133
PROCESSING PARAMETER VALUE UNIT PARAMETER NORM
Nozzle temperature 260 – 290 C
Max. melt temperature 300 C
Print bed temperature 80 – 140 C
Build chamber temperature 80 – 100 C
Nozzle diameter 0,4 – 0,6 mm
Print speed 30 – 50 mm/s
Fan speed 0 %
PREDRYING VALUE UNIT PARAMETER NORM
Drying temperature 80 C
Drying time 8 h